Carbon Graphite Rod Black Round Graphite Bar Conductive Lubricating Rod
Technical Parameter
| Item | Unitas | Classis | ||||||
| Maximam particulam |
| 2.0mm | 2.0mm | 0.8mm | 0.8mm | 25-45μm | 25-45μm | 6-15μm |
| Resistentia | ≤uΩ.m | 9 | 9 | 8.5 | 8.5 | 12 | 12 | 10-12 |
| Compressive vires | ≥Mpa | 20 | 28 | 23 | 32 | 60 | 65 | 85-90 |
| Flexurae vires | ≥Mpa | 9.8 | 13 | 10 | 14.5 | 30 | 35 | 38-45 |
| mole densitatis | g/cm3 | 1.63 | 1.71 | 1.7 | 1.72 | 1.78 | 1.82 | 1.85-1.90 |
| CET(100-600°C) | ≤×10-6/°C | 2.5 | 2.5 | 2.5 | 2.5 | 4.5 | 4.5 | 3.5-5.0 |
| Cineres | ≤% | 0.3 | 0.3 | 0.3 | 0.3 | 250-1000 ppm | 250-1000 ppm | 150-800 ppm |
| Calor conductivity coefficientis | W/mk | 120 | 120 | 120 | 120 |
|
| |
Descriptio
Particulae optimae optimae conductivity et caliditas resistentiae habent et maxime adhibentur in industria chemica ad diversas necessitates emptoris occurrendas.Iuxing Carbonis particulas subtilissimas secundum exigentias emptoris mos est ut in tuto collocet ut perfectum opus recipiant.Contra, crassae particulae densitatem et vim bonam habent et ut materias conductivas ad applicationes mechanicas adhibentur.
Applications
Virgae graphitae communiter in industriis utuntur ut aerospace, electronica, industria, et vestibulum.In aerospace industria, graphitae virgae adhibentur ad calefaciendum scuta, nozzles erucae, et alia quae altas scelerisque conductivity et vires requirunt.In industria electronicorum hae virgae adhibentur ut electrodes, calor deprimatur, et alia elementa quae optimum electrica conductivity requirunt.
commoda
- Particula tenuis
- Bonum electrica conductivity
- Princeps caliditas resistentia
- Crassum particula
- Bonum density virtus
Lorem praebemus magnitudinum secantium ad graphitas virgas fabricandas quae certis requisitis tuis occurrunt.Cum capacitate productionis nostra valida, amplis diametris productis quae ab 50mm ad 1200mm vagantibus suppeditare possumus.
Cum virgas graphitas eligens, interest eorum proprietates et facultates considerare.Variae graphitae materiae rudis genera in variis proprietatibus in producto finali provenient.Verbi gratia, virgae graphitae naturales notae sunt propter altitudinem conductivitatis, cum baculi graphitici synthetici maiorem vim ac vetustatem habent.
Related Products
-
Silicon Carbide Graphite Crucible M.
Silicon Carbide Crucible Property Item Sic Content Tempeatue esistance Cabon Content Appaent Poosity Mole Densitas Data ≥48% ≥1650°C ≥30%-45% ≤%18-%25 ≥1.9-2.1g/cm3 Nota: Aptare possumus contentum unaquaque aw mateialis ad po- tuendum cucullum accomodatum consuetudinum equiementum.Silicon Cabide Cucible Commoda Maximum sength Bonum themal conductivity Low themal expansion High calor esistance High stength ...
-
High Purity Sic Silicon Carbide Crucible Graphi...
Silicon Carbide Crucible euismod Parameter Data Parameter Data SiC ≥85% Frigus Contritionis Fortitudo ≥100MPa SiO₂ ≤10% Apparens Porosity ≤%18 Fe₂O₃ <1% Temperature Repugnantia ≥1700°C Mole Densitas ≥2.60 g/cm³ Producere possumus secundum exigentiam Descriptio Lorem Optimum scelerisque conductivity---It has excellent scelerisque...
-
Silicon Graphite Crucible For Metal Melling Cla...
Technical Parameter For Clay Graphite Crucible SIC C Modulus Rupturae Temperaturae Repugnantia Molis Densitas Apparens Porositas ≥ 40% ≥ 35% ≥10Mpa 1790℃ ≥2.2 G/CM3 ≤15% Nota: Accommodare possumus contentum cuiusque materiae rudis ad producendum uas secundum clientium postulationem.Descriptio graphita in his uasculis adhibita fieri solet...
-
Carbon Blocks Extruded Graphite obstruit Edm Isos ...
Parameter Technical Parameter Physicus And Chemical Indices For Graphite Clausus Item Unit GSK TSK PSK Granule mm 0.8 2.0 4.0 Densitas g/cm3 ≥1.74 ≥1.72 ≥1.72 Resistivity μ Ω.m ≤7.5 ≤8 ≤8.5 Fortitudo Compressiva Mpa ≥36 ≥35 ≥34 Fraxinus % ≤0.3 ≤0.3 ≤0.3 Elasticae Modulus Gpa ≤8 ≤7 ≤6 CTE 10-6/℃ ≤3 ≤2.5 ≤2 Flexurae Virtutis Mpa 15 14.5 14 Porositas % ≥...
-
Pii Carbide Sic graphite fusorium pro melti ...
Silicon Carbide Crucible euismod Parameter Data Parameter Data SiC ≥85% Frigus Contritionis Fortitudo ≥100MPa SiO₂ ≤10% Apparens Porosity ≤%18 Fe₂O₃ <1% Temperature Repugnantia ≥1700°C Mole Densitas ≥2.60 g/cm³ Producere possumus secundum exigentiam Descriptio Lorem Ut quaedam refractione producta progressa, Silicon carbide...