UHP 450mm Fornax Graphite Electrodes Cum Papillis T4L T4N 4TPI
Technical Parameter
| Parameter | Pars | Unitas | UHP 450mm (18") Data |
| Nominal Diameter | Electrode | mm (inch) | 450 (18). |
| Max Diameter | mm | 460 | |
| Min Diameter | mm | 454 | |
| Longitudo nominal | mm | 1800/2400 | |
| Max Longitudo | mm | 1900/2500 | |
| Min Longitudo | mm | 1700/2300 | |
| Max Current Densitas | KA/cm2 | 19-27 | |
| Current Capacitas baiulans | A | 32000-45000 | |
| Imprimis resistentia | Electrode | μΩm | 4.8-5.8 |
| Papilla | 3.4-3.8 | ||
| Flexurae Fortitudo | Electrode | Mpa | ≥12.0 |
| Papilla | ≥22.0 | ||
| Modulus | Electrode | Gpa | ≤13.0 |
| Papilla | ≤18.0 | ||
| mole Density | Electrode | g/cm*3 | 1.68-1.72 |
| Papilla | 1.78-1.84 | ||
| CTE | Electrode | 10-6/ | ≤1.2 |
| Papilla | ≤1.0 | ||
| Cinis Content | Electrode | % | ≤0.2 |
| Papilla | ≤0.2 |
NOTE: Quaelibet specifica exigentia in dimensione offerri potest.
Applications
Ultra vim altam (UHP) electrodes graphitae adhibentur in applicationibus fornaces electrica arcus producentibus ferrum qualitatem et alia metalla.Etiam in variis industriis late adhibentur, inter potentiam nuclearem, metallurgiam, oeconomiam, et plura. UHP Electrode Graphite etiam propter altam vim mechanicam et machinam accurate cognoscitur.Hoc efficit ut electrodes graphitae satis valeant intensas vires et pressuras intra fornacem sustinere, servata eorum figura et magnitudine.Gufan studet producere electrode graphite graphite late amplis ut exigentii laboris superioris efficientiae et humilitatis totius sumptus pro omnibus mundi clientibus.
Productio Processus Chart
Inquisitionem nobis mitte electronicam, contactum faciemus cum te cum tuam electronicam accipimus, vel me contactum in app chat.
Ita vero facimus.Notae naves designari possunt et typis mandari sicut postulationem tuam.
Solet traditio tempus est 10 ad 15 dies post solutionem vel contractum subscriptionis.Vel partus tempus agi potest, si mense vel alio speciali tempore liberare opus est.
Related Products
-
UHP 400mm Turkey Graphite Electrode For EAF LF ...
Parameter technicus Parameter Pars Unit UHP 400mm(16") Data Nominalis Diameter Electrode mm (inch) 400(16) Max Diameter mm 409 Min Diameter mm 403 Nominal Longitudo mm 1600/1800 Max Longitudo mm 1700/1900 Min Longitudo mm 1500/1700 Max Current Densitas KA/cm2 16-24 Current Capacitas Capacitas A 25000-40000 Imprimis resistentia Electrode μΩm 4.8-5.8 Papilla 3.4-4.0 F...
-
Carbon Blocks Extruded Graphite obstruit Edm Isos ...
Parameter Technical Parameter Physicus And Chemical Indices For Graphite Clausus Item Unit GSK TSK PSK Granule mm 0.8 2.0 4.0 Densitas g/cm3 ≥1.74 ≥1.72 ≥1.72 Resistivity μ Ω.m ≤7.5 ≤8 ≤8.5 Fortitudo Compressiva Mpa ≥36 ≥35 ≥34 Fraxinus % ≤0.3 ≤0.3 ≤0.3 Elasticae Modulus Gpa ≤8 ≤7 ≤6 CTE 10-6/℃ ≤3 ≤2.5 ≤2 Flexurae Virtutis Mpa 15 14.5 14 Porositas % ≥...
-
Carbon Additive Carbon Raiser for Ferro Iactum...
Calcinatum Petroleum Coke (CPC) Compositio Carbonis (FC) volatilis Materia (VM) Sulphur(S) Humor cinerum ≥96% ≤1% 0≤0.5% ≤0.5% ≤0.5% Size: 0-1mm, 1-3mm, 1 -5mm vel clientium optio sarcina: 1.Waterproof PP saccis contextis, 25 kgs per sacculum chartaceum, 50 kgs per saccos parvos 2.800kgs-1000kgs per sacculum ut saccos IMPERVIUS jumbo Quomodo producere Calcined Petroleum Coke (CPC) Ache...
-
Graphite Carbon Electrodes For Submerged Electr...
Technical Parameter Parameter Part Unitas RP 350mm(14") Data Nominalis Diameter Electrode(E) mm (inch) 350(14) Max Diameter mm 358 Min Diameter mm 352 Nominal Longitudo mm 1600/1800 Max Longitudo mm 1700/1900 Min Longitudo mm 1500 /1700 Max Current Densitas KA/cm2 14-18 Current Capacitas A 13500-18000 Imprimis resistentia Electrode (E) μΩm 7.5-8.5 Nipple (N) 5.8...
-
High Density Small Diameter Fornax Graphite El...
Technical Parameter Chart 1:Technical Parameter For Small Diameter Graphite Electrode Diameter Pars Resistentia Flexuralis Fortitudo Modulus Densitas CTE Cinerum Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55 -1.64 ≤2.4 ≤0.3 Papilla 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55-1.64 ≤2.4 ≤0.3 Nip...
-
Silicon Graphite Crucible For Metal Melling Cla...
Technical Parameter For Clay Graphite Crucible SIC C Modulus Rupturae Temperaturae Repugnantia Molis Densitas Apparens Porositas ≥ 40% ≥ 35% ≥10Mpa 1790℃ ≥2.2 G/CM3 ≤15% Nota: Accommodare possumus contentum cuiusque materiae rudis ad producendum uas secundum clientium postulationem.Descriptio graphita in his uasculis adhibita fieri solet...