Ultra High Power UHP 650mm Fornace Graphite Electrode For Smelting Steel
Technical Parameter
| Parameter | Pars | Unitas | UHP 650mm(26") Data |
| Nominal Diameter | Electrode | mm (inch) | 650 |
| Max Diameter | mm | 663 | |
| Min Diameter | mm | 659 | |
| Longitudo nominal | mm | 2200/2700 | |
| Max Longitudo | mm | 2300/2800 | |
| Min Longitudo | mm | 2100/2600 | |
| Max Current Densitas | KA/cm2 | 21-25 | |
| Current Capacitas baiulans | A | 70000-86000 | |
| Imprimis resistentia | Electrode | μΩm | 4.5-5.4 |
| Papilla | 3.0-3.6 | ||
| Flexurae Fortitudo | Electrode | Mpa | ≥10.0 |
| Papilla | ≥24.0 | ||
| Modulus | Electrode | Gpa | ≤13.0 |
| Papilla | ≤20.0 | ||
| mole Density | Electrode | g/cm*3 | 1.68-1.72 |
| Papilla | 1.80-1.86 | ||
| CTE | Electrode | 10-6/ | ≤1.2 |
| Papilla | ≤1.0 | ||
| Cinis Content | Electrode | % | ≤0.2 |
| Papilla | ≤0.2 |
NOTE: Quaelibet specifica exigentia in dimensione offerri potest.
Product Feature
Electrode graphite ultra potestatem altam scelerisque conductivity altam habet et calori et ictum valde repugnat. Maxime ad usum fornacis arcus electrici ultra summam potestatem (EAC).Densitas hodierna maior plus quam 25A/cm2.Diameter principalis 300-700mm est, quae efficientiam melioris productionis et gratuita minuit.
UHP electio idonea et optima est ad fornacem electrici arcus ultra-altae potentiae 500~1200Kv.A/t per ton. UHP graphite electrode physico et chemico index melior est quam RP, HP graphite electrode. tempus faciendi, augendi efficientiam producendi.
Product Applicationem
Operatio graphite UHP electrodis non solum ad industriam ferri contrahitur.Habet amplis applicationes, incluso fornacem electricam fornacem excoquunt, chalcitiam excoquunt, calcium carbide excoquunt, et aluminium excoquunt.Eius mobilitas testamentum est ad superiora facienda et potentia ad verteret non solum industriam ferrum, sed etiam alias industrias.
UHP Graphite Electrode Current Capacitas Charta
| Nominal Diameter | Ultra High Power (UHP) Graphite Electrode | ||
| mm | Inch | Current Capacitas baiulans (A) | Current Density (A / cm2) |
| 300 | 12 | 20000-30000 | 20-30 |
| 350 | 14 | 20000-30000 | 20-30 |
| 400 | 16 | 25000-40000 | 16-24 |
| 450 | 18 | 32000-45000 | 19-27 |
| 500 | 20 | 38000-55000 | 18-27 |
| 550 | 22 | 45000-65000 | 18-27 |
| 600 | 24 | 52000-78000 | 18-27 |
| 650 | 26 | 70000-86000 | 21-25 |
| 700 | 28 | 73000-96000 | 18-24 |
Gufan Carbon utitur coke acus qualis summus ex USA, Iaponia et UK importata est.
In statu, Gufan maxime facit electrum graphiteum electrum incluso gradu UHP,HP,RP, a diametro 200mm(8") ad 700mm(28"). quae usui possunt in fornace electrica.Magnae diametri, ut UHP700, UHP650 et UHP600, a nostris clientibus bonas opiniones accipiunt.
Related Products
-
Electric Arc Furnace Graphite Electrodes HP550m...
Technical Parameter Parameter Pars Unit HP 550mm(22") Data Nominalis Diameter Electrode mm(inch) 550 Max Diameter mm 562 Min Diameter mm 556 Nominal Longitudo mm 1800/2400 Max Longitudo mm 1900/2500 Min Longitudo mm 1700/2300 Densitas Current KA/ cm2 14-22 Current Capacitas Capacitas A 34000-53000 Imprimis resistentia Electrode μΩm 5.2-6.5 Papilla 3.2-4.3 Flexurale S...
-
Carbon Graphite Rod Black Graphite Bar Co...
Parameter Technical Item Unit Classis Maximum Particula 2.0mm 2.0mm 0.8mm 0.8mm 25-45μm 25-45μm 6-15μm Resistentia ≤uΩ.m 9 9 8.5 8.5 12 12 10-12 ≥Mpa 20 28 23 32 60 65 85- 90 Flexurae robur ≥Mpa 9.8 13 10 14.5 30 35 38-45 Molis densitatis g/cm3 1.63 1.71 1.7 1.72 1.78 1.82 1.85-1.90 CET(100-600°C) ≤×10-6/°C 2.5 ...
-
Parvus Diameter Fornax Graphite Electrode for e...
Technical Parameter Chart 1:Technical Parameter For Small Diameter Graphite Electrode Diameter Pars Resistentia Flexuralis Fortitudo Modulus Densitas CTE Cinerum Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55 -1.64 ≤2.4 ≤0.3 Papilla 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55-1.64 ≤2.4 ≤0.3 Nip...
-
Graphite Electrode Usus Ad Corundum Refining E...
Technical Parameter Chart 1:Technical Parameter For Small Diameter Graphite Electrode Diameter Pars Resistentia Flexuralis Fortitudo Modulus Densitas CTE Cinerum Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55 -1.64 ≤2.4 ≤0.3 Papilla 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55-1.64 ≤2.4 ≤0.3 Nip...
-
UHP 500mm Dia 20 Inch Fornax Graphite Electrod...
Technical Parameter Physica & Chemical Properties For D500mm(20") Electrode & Nipple Parameter Part Unit UHP 500mm(20") Data Nominal Diameter Electrode mm(inch) 500 Max Diameter mm 511 Min Diameter mm 505 Nominal Longitudo mm 1800/2400 Max Longitudo mm 1900/2500 Min Longitudo mm 1700/2300 Max Current Densitas KA/cm2 18-27 Current Capacitas Capacitas A 38000-55000 Sp...
-
HP24 Graphite Carbon Electrodes Dia 600mm Elec...
Technical Parameter Parameter Part Unitas HP 600mm(24") Data Nominalis Diameter Electrode mm (inch) 600 Max Diameter mm 613 Min Diameter mm 607 Nominal Longitudo mm 2200/2700 Max Longitudo mm 2300/2800 Min Longitudo mm 2100/2600 Current Density KA/ cm2 13-21 Current Capacitas A 38000-58000 Imprimis resistentia Electrodis μΩm 5.2-6.5 Papilla 3.2-4.3 Flexurale S...