UHP 350mm Graphite Electrodes In Electrolysis enim Smelting Steel
Technical Parameter
| Parameter | Pars | Unitas | UHP 350mm(14") Data |
| Nominal Diameter | Electrode | mm (inch) | 350 (14) |
| Max Diameter | mm | 358 | |
| Min Diameter | mm | 352 | |
| Longitudo nominal | mm | 1600/180 | |
| Max Longitudo | mm | 1700/1900 | |
| Min Longitudo | mm | 1500/1700 | |
| Max Current Densitas | KA/cm2 | 20-30 | |
| Current Capacitas baiulans | A | 20000-30000 | |
| Imprimis resistentia | Electrode | μΩm | 4.8-5.8 |
| Papilla | 3.4-4.0 | ||
| Flexurae Fortitudo | Electrode | Mpa | ≥12.0 |
| Papilla | ≥22.0 | ||
| Modulus | Electrode | Gpa | ≤13.0 |
| Papilla | ≤18.0 | ||
| mole Density | Electrode | g/cm*3 | 1.68-1.72 |
| Papilla | 1.78-1.84 | ||
| CTE | Electrode | 10-6/ | ≤1.2 |
| Papilla | ≤1.0 | ||
| Cinis Content | Electrode | % | ≤0.2 |
| Papilla | ≤0.2 |
NOTE: Quaelibet specifica exigentia in dimensione offerri potest.
Product Grade
Gradus graphite electrode in potestatem regularem graphite electrodeRP） dividuntur, alta potentia graphite electrode(HP), ultra alta potentia graphite electrode (UHP).
Maxime Application pro Electric Arcus fornacis in Steel Condita
Electrodes graphites pro ferro reddendi rationum 70-80% totius moles applicationis electrodes graphitae. Transeundo altam intentionem et currentem ad electrode graphite, arcus electricus generabitur inter electrum auriculam et faece metallicam quae ingentis caloris exiguo liquefaciet. Processus ustionis graphite electrode consumet et constanter reponi debent.
Electrode graphite UHP vulgo in industria ferri adhibetur in productione fornacis arcus electrici (EAF) ferri. Processus AEF liquescens faecum ferrum involvit ad novum chalybem producendum. Electrode UHP graphite adhibetur ad arcum electricum creare, qui exiguo ferro ad punctum liquescens calefacit. Hic processus efficax et sumptus-efficax est, ut ferrum cito et in magna quantitate permittit produci.
Sectio Videre et Plan Visum de Arco Fornacis Electrical
OPIFICIUM possessores sumus lineae productionis et turmae professionales.
30% TT in antecessum ut pignus, 70% statera TT ante partum.
Related products
-
Graphite Electrode Usus Ad Corundum Refining E...
Technical Parameter Chart 1:Technical Parameter For Parvus Diameter Graphite Electrode Diameter Pars Resistentia Flexuralis Fortitudo Modulus Densitas CTE Cinerum Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55 -1.64 ≤2.4 ≤0.3 Nipple 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55-1.64 ≤2.4 ≤0.3 Nip...
-
Soderberg Carbon Electrode Paste pro Ferroallo...
Technical Parameter Item Sealed Electrode Past Standard Electrode Paste GF01 GF02 GF03 GF04 GF05 Volatile Flux(%) 12.0-15.5 12.0-15.5 9.5-13.5 11.5-15.5 11.5-15.5 Compressive Strength(Mpa) 18.0 17.0 22.0 21.0 20.0 Resisitivity(uΩm) 65 75 80 85 90 Volum Densitas (g/cm3) 1.38 1.38 1.38 1.38 1.38 Longitudo(%) 5-20 5-20 5-30 15-40 15-40 Cinerum(%) 4.0 6.0 ...
-
High Density Small Diameter Fornax Graphite El...
Technical Parameter Chart 1:Technical Parameter For Parvus Diameter Graphite Electrode Diameter Pars Resistentia Flexuralis Fortitudo Modulus Densitas CTE Cinerum Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55 -1.64 ≤2.4 ≤0.3 Nipple 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55-1.64 ≤2.4 ≤0.3 Nip...
-
Regular Power Small Diameter Graphite Electrode...
Technical Parameter Chart 1:Technical Parameter For Parvus Diameter Graphite Electrode Diameter Pars Resistentia Flexuralis Fortitudo Modulus Densitas CTE Cinerum Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55 -1.64 ≤2.4 ≤0.3 Nipple 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55-1.64 ≤2.4 ≤0.3 Ni...
-
Fornax Graphite Electrode Small Diameter 75mm ...
Technical Parameter Chart 1:Technical Parameter For Parvus Diameter Graphite Electrode Diameter Pars Resistentia Flexuralis Fortitudo Modulus Densitas CTE Cinerum Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55 -1.64 ≤2.4 ≤0.3 Nipple 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55-1.64 ≤2.4 ≤0.3 Nip...
-
Z Sulfur FC 93% Carburizer Carbon Raiser Iro...
Graphite Petroleum Coke (GPC) Compositio carbonis fixa (FC) Materia volatilis (VM) Sulphur(S) Fraxinus Nitrogen(N) Hydrogenium (H) Humidum ≥98% ≤1% 0≤0.05% ≤1% ≤0.03% ≤0.01% ≤0.5% ≥98.5% ≤0.8% ≤0.05% ≤0.7% ≤0.03% ≤0.01% ≤0.5% ≥99% ≤0.5% ≤0.03% ≤0.5% ≤0.03% ≤0.01% ≤0.5% Size: 0-0.50mm, 5-1mm, 1-3mm, 0-5mm, 1-5mm, 0-10mm , 5-10mm, 5-10mm, 10-15mm vel optionis clientium stipare: 1. Waterproof...